Descripción
Polymer-modified cementitious mortar for leveling pavements between 3-50 mm. Very low emission cement-based self-leveling compound, suitable for indoor areas. Sikafloor-200 is characterized by being a multipurpose leveling compound, for medium loads, with very low shrinkage and high thickness.
Suitable for filling, smoothing and leveling suitable substrates before applying parquet, ceramic tiles, textile and elastic floor coverings in residential and non-industrial interior areas.
ADVANTAGES
- Self-leveling
- Suitable for application in underfloor heating systems
- Low voltage
- Pumpable
- Suitable for building adhered screeds under ceramic tiles on cementitious supports
PRODUCT INFORMATION
- Chemical base based on cement, modified with polymers
- Conservation: 12 months from the date of manufacture
- Storage conditions: Open bags should be closed immediately and consumed as soon as possible. Do not store below +5°C.
- Gray
TECHNICAL INFORMATION
- Compressive Strength: ~25 N/mm2 (28 days at 23 °C)
- Flexural Strength: ~6 N/mm2 (28 days at 23 °C)
- Thermal Conductivity: 1.5 W/mk
APPLICATION
- Mixing ratio: ~4.5 L of water per 25 kg Sikafloor®-200 Level
- Density of fresh mortar: ~2.05 kg/dm3
- Layer Thickness: 3–50 mm
- Ambient temperature: +5 °C min. / +30 °C max.
- Relative Air Humidity: < 75%
- Support temperature: +5 °C min. / +30 °C max.
- Mix life: ~30 min. at +20 °C
- Consumption: ~ 1.74 kg/m2/mm
- Waiting Time/Repaintability:
| COVERING | THICKNESS | STANDBY TIME |
| Tiles, textiles, vinyl coverings, LVT and linoleum | >10mm | >24 hours |
| Resin flooring | >10mm | >48 hours |
| Tiles, textiles, vinyl coverings, LVT and linoleum | >50mm | >72 hours |
| Resin flooring | >50mm | >72 hours |
(All values are approximate and subject to variation. Values given at 20 °C and 65% relative humidity, support temperature +15 °C).